■ package specification

18 kg / barrel.

■ technical indicators

The color and appearance of the paint film shall comply with the standard template and be flat and smooth

Viscosity (coated 4# cup, 23 ± 2 ℃), s ≥ 60

Fineness, um ≤ 40

Drying time,

Surface dry (23 ± 2 ℃) ≤ 1H

Practical drying (23 ± 2 ℃) ≤ 12h

Flexibility, mm ≤ 2

Adhesion (circle drawing method), grade ≤ 2

The artificial accelerated aging (quv340300h) shall not blister or peel off, and the color and luster are allowed to change

■ matching paint

Iron red epoxy antirust paint iron red epoxy antirust paint

Micaceous iron epoxy antirust paint zinc rich epoxy quick drying antirust primer (sub assembly)

Iron red zinc phosphate epoxy primer (sub assembly) steel structure epoxy primer (sub assembly)

■ main purpose

It is suitable to be used as anti-corrosion protective finish on the surfaces of various construction machinery, large building steel components, etc. it can also be used as protective paint for upper and lower painting of ship waterline.

■ surface treatment

The previous coat of paint shall be thoroughly dry to remove all oil stains and sundries on the paint film.

■ painting reference

Paint density: white 1.00-1.20g/cm3, aluminum 1.10-1.21g/cm3

Theoretical dosage: 120 - 180g / m2 (film thickness 50um, excluding loss)

Diluent diluent

Coating parameters

Air spraying

The nozzle diameter is about 2.0-2.5mm

Air pressure 0.3 - 0.4MPa (about 3 - 4kg / cm2)

■ storage and transportation

The product shall be stored in a cool, dry and ventilated place to prevent direct sunlight, isolate the fire source and keep away from the heat source. The storage period of paint is 12 months. During transportation, the products shall be protected from rain, sunlight and collision, and shall comply with the transportation regulations of the transportation department on dangerous chemicals.

■ precautions

1. The substrate temperature must be above 3 ℃ above the dew point.

2. This product is not suitable for use under high temperature (60 ℃).